Description
Kimya ABS Kevlar 3D Filament 1.75mm 500g
The Kimya ABS Kevlar 3D filament belongs to the styrenic polymer family. Acrylonitrile Butadiene Styrene Kevlar (ABS Kevlar) is a composite filament enriched in aramid fibers. It offers properties that are superior to a standard ABS. It provides the printed parts with increased resistance to abrasion. It is used for finished parts and tools. The Kimya ABS Kevlar 3D filament has the following properties:
- Low warpage – compared to ABS-S-
- Lighter-weight printed parts – compared to ABS Carbon-
- Complies with the REACH standard
Diameter: 1.75mm
Net Weight: 500g
Color: Black
Specifications
FILAMENT PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
|---|---|---|
|
Diameter |
INS-6712 |
1.75 ± 0.1 mm 2.85 ± 0.1 mm |
|
Density |
ISO 1183-1 |
1.037 g/cm3 |
|
Moisture rate |
INS-6711 |
< 1 % |
|
Melt flow index (MFI) |
ISO 1133-1 (@220°C – 10 kg) |
14.8 g/10min |
|
Glass transition temperature (Tg) |
ISO 11357-1 DSC (10°C/min – 20-220°C) |
100 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION | XY |
|---|---|
| Printing Speed | 40-70 mm/s |
| Infill | 100% – rectilinear |
| Infill Angle | 45°/-45° |
| Nozzle Temperature | 250-270°C |
| Bed T° | 90-110°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES | |
|---|---|---|---|
| MECHANICAL PROPERTIES | Tensile modulus | ISO 527-2/5A/50 | 1,775 MPa |
| Tensile Strength | ISO 527-2/5A/50 | 31.1 MPa | |
| Tensile strain at strength | ISO 527-2/1A/50 | 2 % | |
| Tensile Stress at Break | ISO 527-2/5A/50 | 27.7 MPa | |
| Tensile strain at break | ISO 527-2/5A/50 | 4 % | |
| Flexural modulus | ISO 178 | 1,509 MPa | |
| Flexural strength* | ISO 178 | > 5 % | |
| Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 44.7 MPa | |
| Charpy impact resistance | ISO 179-1/1eA | 8 kJ/m² | |
| Shore Hardness | ISO 868 | 65,2D |